Causes of cracks of chemical apparatus made of austenitic steel
##plugins.themes.bootstrap3.article.sidebar##
##plugins.themes.bootstrap3.article.main##
Abstrakt
The subject of the research was the installation of a water steam used in the chemical industry. Penetration tests revealed an extensive network of cracks on the surface of steel and welds. Metallographic studies, chemical composition analysis, EDX anal-ysis were performed. Thermal treatment of steel was carried out and microhardness measurements were made. The results of the tests showed that stress corrosion was the main reason for the occurrence of cracks.
Pobrania
##plugins.themes.bootstrap3.article.details##
Creative Commons CC BY 4.0 https://creativecommons.org/licenses/by/4.0/
Artykuły czasopisma Welding Technology Review (Przegląd Spawalnictwa) publikowane są w otwartym dostępie na licencji CC BY (licencja Creative Commons Uznanie autorstwa 4.0 Międzynarodowe). Licencja CC BY jest najbardziej otwartą dostępną licencją i uważaną za „złoty standard” w formule otwartego dostępu; jest również preferowany przez wielu fundatorów badań. Licencja ta umożliwia czytelnikom kopiowanie i redystrybucję materiału na dowolnym nośniku i w dowolnym formacie, a także zmienianie, przekształcanie lub budowanie na nim materiału, w tym do użytku komercyjnego, pod warunkiem wskazania oryginalnego autora.
Bibliografia
G. R. Mirshekari, E. Tavakoli, M. Atapour, B. Sadeghian, Microstructure and corrosion behavior of multipass gas tungsten arc welded 304L stainless steel, Materials and Design (2014), 55, 905-911. DOI: https://doi.org/10.1016/j.matdes.2013.10.064
A. Świerczyńska, G. Rogalski, D. Fydrych, Badania struktury i właściwości spawanych austenitycznych rur wymienników ciepła, Welding Technolo- gy Review (2010), vol. 82 (6), 11-16.
K.R.M. Rao, S. Mukherjee, P.M. Raole, I. Manna, Characterization of surface microstructure and properties of low-energy high-dose plasma immersion ion-implanted 304L austenitic stainless steel, Surface and Coating Technology (2005), 200, 2049-2057. DOI: https://doi.org/10.1016/j.surfcoat.2004.06.035
S. Ghosh, V. P. S. Rana, V. Kain, V. Mittal, S.K. Baveja, Role of residual stresses induced by industrial fabrication on stress corrosion cracking susceptibility of austenitic stainless steel Materials & Design (2011), vol. 32 (7), 3823-3831.
E. Tasak, A. Ziewiec, Spawalność materiałów konstrukcyjnych, Wydawnictwo JAK, Kraków (2009).
H. Ezuber, A. Alshater, S. O. Nisar, A. Gonsalvez, S. Aslam, Effect of Surface Finish on the Pitting Corrosion Behavior of Sensitized AISI 304 Austenitic Stainless Steel Alloys in 3.5% NaCl Solutions, Surface Engineering and Applied Electrochemistry (2018), 54, 73-80 DOI: https://doi.org/10.3103/S1068375518010039
R. E. Melchers, I. A. Chaves, R. Jeffrey, A Conceptual Model for the Interaction between Carbon Content and Manganese Sulphide Inclusions in the Short-Term Seawater Corrosion of Low Carbon Steel, Metals (2016), vol.6 (6), 132.
T. Prosek, A. Iversen, C. Taxn, D. Thierry, Low-Temperature Stress Corrosion Cracking of Stainless Steels in the Atmosphere in the Presence of Chloride Deposits, CORROSION (2009), vol. 65 (2), 105-117.
S. Ghos, , V. P. S. Rana, V. Kain, V. Mittal, S.K. Baveja, Role of residual stresses induced by industrial fabrication on stress corrosion cracking susceptibility of austenitic stainless steel, Materials and Design (2011), 32, 3823-3831. DOI: https://doi.org/10.1016/j.matdes.2011.03.012
P. Roffey, E. H. Davies, The generation of corrosion under insulation and stress corrosion cracking due to sulphide stress cracking in an austenitic stainless steel hydrocarbon gas pipeline, Engineering Failure Analysis (2014), 44, 148-157. DOI: https://doi.org/10.1016/j.engfailanal.2014.05.004
PN-H-86020:1971 Stal odporna na korozję (nierdzewna i kwasoodporna) Gatunki.
PN-EN 10028-7:2016-09 wyroby płaskie ze stali na urządzenia ciśnieniowe Część 7: Stale odporne na korozję
I.I. Vasilenko, R.K. Melehov, Korrozionnoe rastreskivanie stali, Kiev (1977) (ВаÑиленко И.И., Мелехов Ð .К.: Коррозионное раÑтреÑкивание Ñталей, Киев 1977).
G. Rogalski, J. Łabanowski, D. Fydrych, A. Świerczyńska, Wpływ obróbki cieplnej na właściwości spawanych austenitycznych rur wymienników ciepła, Welding Technology Review (2014), vol. 86 (6), 24-31.