Attempts of braze welding galvanized steel with a trifocal multi-beam laser system
##plugins.themes.bootstrap3.article.main##
Abstrakt
The paper presents the evaluation of the brazing capabilities of the multi-beam Trifocal laser joint system made of galvanized steel DX51D with a thickness of 3 mm, covered with a protective coating of Magnelis type. The brazed joints obtained have been subjected to metallographic, strength and corrosion resistance tests in the Ascott CCIP450 salt cell. The tests have shown that there is a certain range of brazing process parameters that allow to make the correct overlap joints of high quality with small welding distortions and a narrow heat affected zone. The obtained joints are characterized by a slightly worse corrosion resistance than the basic material, and zinc evaporation by means of additional low-power laser beams improves the solder's flow.
Pobrania
##plugins.themes.bootstrap3.article.details##
Creative Commons CC BY 4.0 https://creativecommons.org/licenses/by/4.0/
Artykuły czasopisma Welding Technology Review (Przegląd Spawalnictwa) publikowane są w otwartym dostępie na licencji CC BY (licencja Creative Commons Uznanie autorstwa 4.0 Międzynarodowe). Licencja CC BY jest najbardziej otwartą dostępną licencją i uważaną za „złoty standard” w formule otwartego dostępu; jest również preferowany przez wielu fundatorów badań. Licencja ta umożliwia czytelnikom kopiowanie i redystrybucję materiału na dowolnym nośniku i w dowolnym formacie, a także zmienianie, przekształcanie lub budowanie na nim materiału, w tym do użytku komercyjnego, pod warunkiem wskazania oryginalnego autora.
Bibliografia
Pilarczyk J., Banasik M., Stano S., Dworak J., Laser joining with wire filler material and mechanical seam tracking system, Welding Technology Review, 2011, Vol. 83(12), 9-14.
Mathieu A., Pontevicci S., Viala J., Cicala E., Grevey D., Laser brazing of a steel/aluminum assembly with hot filler wire, Material Science and Engineering:A, 2006, Vol. 435-436, 19-28.
Mathieu A., Pontevicci S., Viala J., Cicala E., Grevey D., Temperature control in laser brazing of a steel assembly using thermographic measurements, NDT&E International, 2006, Vol. 39(4), 272-276.
Reimann W., Dobler M., Goede M., Dilger K., Three-beam laser brazing of zinc-coated steel, The International Journal of Advanced Manufacturing Technology, 2017, Vol. 90(1-4), 317-328.
Chmielewski T., Golański D., Włosiński W., Zimmerman J., Utilizing the energy of kinetic friction for the metallization of ceramics, Bulletin of the Polish Academy of Sciences Technical Sciences, 2015, Vol. 63(1), 201-207.
Zhang M., Chen G., Zhang Y., Wu K., Research on microstructure and mechanical properties of laser keyhole welding-brazing of automotive galvanized steel to aluminium alloy, Materials & Design, 2013, Vol. 45, 24-30.
Chudziński M., Nowacki J., Zmitrowicz P., Lutowanie w budowie maszyn, Wydawnictwo Naukowe PWN, 2008, Warszawa.
Dobrzański L.A., Warstwy powierzchniowe kształtowane z wykorzystaniem technologii laserowych, Wydawnictwo Politechniki Śląskiej, 2013, Gliwice.
Klocke F., Frank S., Surface deposits in laser brazing, Science and Technology of Welding and Joining, 2003, Vol. 18(1), 62-69.
Godec B., Grdun V., Braze welding of galvanised steel pipes, Welding World, 2013, Vol. 45, 49-56.
Klimpel A., Czupryński A., Górka J., Lutospawanie metodą GMA cienkich blach ocynkowanych, Welding Technology Review, 2006, Vol. 78(9-10), 72-75.
Klimpel A., Czupryński A., Górka J., Lutospawanie laserowe ocynkowanych stalowych blach karoseryjnych, Biuletyn Instytutu Spawalnictwa, 2006, Vol. 50(6), 39-43.
Füssel U., Zschetzsche J., Szieslo U., Plasmalöten mit stromführendem Zusatzwerkstoff, Der Praktiker, 2002, Vol. 54(10), 336-340.
Draugelates U., Bouaifi B., Plasma-arc brazing: A low-energy joining technique for sheet metal, Welding Journal, 2002, Vol. 81(3), 38-42.
Chmielewski T., Siwek P., Chmielewski M., Piątkowska A., Grabias A., Golański D., Structure and selected properties of arc sprayed coatings containing in-situ fabricated Fe-Al intermetallic phases, Metals, 2018, Vol. 8(12), 1059.
Adamiak M., Wyględacz B., Czupryński A., Górka J., A study of susceptibility and evaluation of causes of cracks formation in braze-weld filler metal in lap joints aluminum carbon steel made with use of CMT Method and High Power Diode Laser, Archives of Metallurgy and Materials, 2017, Vol. 62(4), 2113-2123.