Comparison of abrasion resistance of wear plates
##plugins.themes.bootstrap3.article.sidebar##
##plugins.themes.bootstrap3.article.main##
Abstrakt
In this article results of abrasive wear resistance of a few different steel wear plates made by domestic and foreign producers in technology of automatic FCAW and manual arc (MMAW) cladding and metallurgical bonding of wear resistant layer with base material were presented. Based on abrasive wear resistance tests according to ASTM G65-00, in regard to reference samples from Hardox 400 steel and hardness measurements according to PN-EN ISO 6508- 1:2016 standard, products with best performance parameters on metal-mineral abrasion conditions were chosen.
Pobrania
##plugins.themes.bootstrap3.article.details##
Creative Commons CC BY 4.0 https://creativecommons.org/licenses/by/4.0/
Artykuły czasopisma Welding Technology Review (Przegląd Spawalnictwa) publikowane są w otwartym dostępie na licencji CC BY (licencja Creative Commons Uznanie autorstwa 4.0 Międzynarodowe). Licencja CC BY jest najbardziej otwartą dostępną licencją i uważaną za „złoty standard” w formule otwartego dostępu; jest również preferowany przez wielu fundatorów badań. Licencja ta umożliwia czytelnikom kopiowanie i redystrybucję materiału na dowolnym nośniku i w dowolnym formacie, a także zmienianie, przekształcanie lub budowanie na nim materiału, w tym do użytku komercyjnego, pod warunkiem wskazania oryginalnego autora.
Bibliografia
Kato K.: Abrasive wear of metals, Tribology International, 1997, nr 5, pp. 333-338.
Stachowiak G.W.: Particle angularity and its relationship to abrasive and erosive wear, Wear, 2000, nr 241, pp. 214-219.
Zum Gahr K.H.: Wear by hard particles. Tribology International, 1998, nr 10, pp. 587-596.
Gawrysiuk W.: Płyty trudnościeralne. Technologie wytwarzania i walory eksploatacyjne, Matriały seminaryjne Instytutu Spawalnictwa w Gliwicach.
Stachowiak G.B., Stachowiak G.W.: The effects of particle characteristics on three-body abrasive wear, Wear, 2001, nr 249, pp. 201-207.
Ma X., Liu R., Li D.Y.: Abrasive wear behavior of D2 tool steel with respect to load and sliding speed under dry sand/rubber wheel abrasion condition, Wear, 2000, nr 1, pp. 79-85.
Adamiec P., Gawrysiuk W.: Właściwości warstw napawanych o strukturze żeliw chromowych, Biuletyn Spawalnictwa, Gliwice 2004, nr 2.
Klimpel A., Kik T.: Erosion and abrasion wear resistance of GMA wire surfaced nanostructural deposits, Journal of Archives of Materials Science and Engineering 30(2), April 2008, pp. 121-124.
Adamiak M., Górka J., Kik T.: Comparison of abrasion resistance of selected constructional materials, Journal of Archives of Materials Science and Engineering 37(2), December 2009, pp. 375-380.
ASTM G65-00: Standard Test Method for Measuring Abrasion Using the Dry Sand/Rubber Wheel Apparatus.
Metale Pomiar twardości sposobem Rockwella Część 1: Metoda badania.