Brazing of selected heat-resisting alloys using Ni-Pd filler metal
##plugins.themes.bootstrap3.article.main##
Abstrakt
Pd is a component of some advanced nickel filler metals designed for brazing heat-resisting alloys in order to improve their wettability and to enhance both corrosion resistance and plasticity
of the joints. The joints of Inconel 625, Inconel 718, Hastelloy X, and 410 martensitic stainless steel were prepared by vacuum brazing with NiPd36Cr10BSi filler alloy. Complex structures of the joints were tested. It was revealed the displacement of interfaces from their initial positions in the course of brazing along with active action of Cr, Mo and Nb (for Inconel 718 alloy) in the formation of interstitial layers.
Pobrania
##plugins.themes.bootstrap3.article.details##
Creative Commons CC BY 4.0 https://creativecommons.org/licenses/by/4.0/
Artykuły czasopisma Welding Technology Review (Przegląd Spawalnictwa) publikowane są w otwartym dostępie na licencji CC BY (licencja Creative Commons Uznanie autorstwa 4.0 Międzynarodowe). Licencja CC BY jest najbardziej otwartą dostępną licencją i uważaną za „złoty standard” w formule otwartego dostępu; jest również preferowany przez wielu fundatorów badań. Licencja ta umożliwia czytelnikom kopiowanie i redystrybucję materiału na dowolnym nośniku i w dowolnym formacie, a także zmienianie, przekształcanie lub budowanie na nim materiału, w tym do użytku komercyjnego, pod warunkiem wskazania oryginalnego autora.
Bibliografia
Dul I., Zastosowanie i przetwarzanie stopów niklu w przemyśle lotniczym, Welding Technology Review, 2009, Vol. 81(7-8), 67-73.
Pollock T.M., Alloy design for aircraft engines, Nature Materials, 2016, Vol. 15(8), 809-815.
Davis J.R., ASM Specialty Handbook: Nickel, Cobalt, and Their Alloys, ASM International, Russell Township, 2000.
Babul T., Kondej A., Kowalski S., Baranowski M., Lankiewicz K., Wpływ obróbki powierzchniowej na lutow-ność stali 410. Welding Technology Review, 2016, Vol. 88(3), 14-18.
Baranowski M., Jakubowski J., Lutowność wybranych nadstopów niklu, Welding Technology Review, 2014, Vol. 86(7), 3-8.
Lankiewicz K., Baranowski M., Babul T., Kowalski S., The Study of the Impact of Surface Preparation Methods of Inconel 625 and 718 Nickel-Base Alloys on Wettability by BNi-2 and BNi-3 Brazing Filler Metals, Archives of Metallurgy and Materials, 2015, Vol. 60(1), 159-165. DOI: 10.1515/amm-2015-0025
Baranowski J., Lutowanie twarde w wybranych zastosowaniach w produkcji lotniczej, Welding Technology Review, 2016, Vol. 88(9), 25-28.
Bose D., Datta A., Rabinkin A., De Cristofaro N.J., High Strength Nickel-Palladium-Chromium Brazing Alloys, Welding Journal, 1986, Vol. 65(1), 23-30.
Dul I., Senkara J., Bober M., Jakubowski J., Wpływ wysokotemperaturowego wygrzewania próżniowego na lu-towność Inconelu 718 lutem Palnicro 36, Welding Technology Review, 2013, Vol. 85(9), 15-19.
Baranowski M., Bober M., Kudyba A., Sobczak N., The Effect of Surface Condition on Wetting of HASTEL-LOY® X by Brazing Filler Metal of Ni-Pd-Cr-B-Si System, Journal of Materials Engineering and Performance, 2019, Vol. 28(7), 39503959.
www.espimetals.com.
www.azom.com.
www.morganadvancedmaterials.com.