Welding of heat-treated steel on the example of S690QL
Article Sidebar
Main Article Content
Abstract
The paper presents the technology for welding of heat-treated steel on the example of S690QL steel. Part of the research work shows all relevant parameters and assumptions necessary for the implementation of the welded joint. In addition, part of the research included the results of studies that were conducted on specially prepared specimens. For comparison two butt welds with a thickness of 12 mm and 50 mm and a fillet weld thickness of 40 mm are presented. The scope of research includes the non-destructive testing such as visual test, penetration test, ultrasonic test, radiographic test and destructive tests, which include: tensile test, bending test, impact test, macro test and measurement of hardness.
Downloads
Article Details
Creative Commons CC BY 4.0 https://creativecommons.org/licenses/by/4.0/
Welding Technology Review (WTR) articles are published open access under a CC BY licence (Creative Commons Attribution 4.0 International licence). The CC BY licence is the most open licence available and considered the industry 'gold standard' for open access; it is also preferred by many funders. This licence allows readers to copy and redistribute the material in any medium or format, and to alter, transform, or build upon the material, including for commercial use, providing the original author is credited.
References
Tasak E.: Spawalność stali, Fotobit, Kraków, 2002.
Tasak E.: Metalurgia spawania, Wyd. Jak, Kraków, 2008.
Brózda J.: Stale konstrukcyjne i ich spawalność, Instytut Spawalnictwa, Gliwice, 2008.
Makles K., Spawalność i wybrane właściwości złączy stali ulepszanych cieplnie. Przegląd Spawalnictwa nr 8, 2014, s.19-25