Hybrid Laser Arc Welding HLAW (laser MAG) of 10 mm thickness S700MC steel T-joints
Article Sidebar
Main Article Content
Abstract
In this article examinations of hybrid welding technology (laser beam + MAG) of T-joints from thermomechanically worked high strength steel S700MC 10 mm thick were presented. Joints welded from one side and both sides were made. Carried examinations enabled to classify joints in quality level B according to PN-EN ISO 12932 (Welding. Laser-arc hybrid welding of steels, nickel and nickel alloys. Quality levels for imperfections). In case of one sided weld- ing with partial penetration with beam power of 8.5 kW 8 mm of penetration was achieved without noticeable distortion of web. Double sided joints were characterized with correct geometry. Joint metal is bainitic-ferritic in structure and its hardness rises about 40 HV1 in comparison to base metal hardness (280 HV1). In HAZ a slight softening of material in comparison to base metal is present.
in polish
Spawanie hybrydowe HLAW (wiązka laserowa MAG) złączy teowych blach o grubości 10 mm ze stali S700MC
W artykule przedstawiono badania dotyczące technologii spawania hybrydowego (wiązka laserowa + MAG) złączy teowych stali obrabianej termomechanicznie o wysokiej granicy plastyczności S700MC o grubości 10 mm. Wykonano złącza spawane jednostronne i dwustronne. Przeprowadzone badania nieniszczące pozwoliły sklasyfikować złącza w poziomie jakości B zgodnie z PN-EN ISO 12932 (Spawanie. Spawanie hybrydowe laserowo-łukowe stali, niklu i stopów niklu. Poziomy jakości dla niezgodności). W przypadku spawania jednostronnego z niepełnym przetopem przy zastosowaniu mocy wiązki na poziomie 8,5 kW uzyskano wtopienie na głębokości 8 mm, bez wyraźnego odkształcenia środnika złącza. Uzyskane złącza spawane dwustronnie charakteryzują się poprawną geometrią. Spoina posiada strukturę bainityczno-ferrytyczną, a jej twardość wzrasta o około 40 HV1 w stosunku do twardości materiału rodzimego (280 HV1). W obszarze SWC następuje niewielkie zmiękczenie w stosunku do twardości materiału rodzimego.
Downloads
Article Details
Creative Commons CC BY 4.0 https://creativecommons.org/licenses/by/4.0/
Welding Technology Review (WTR) articles are published open access under a CC BY licence (Creative Commons Attribution 4.0 International licence). The CC BY licence is the most open licence available and considered the industry 'gold standard' for open access; it is also preferred by many funders. This licence allows readers to copy and redistribute the material in any medium or format, and to alter, transform, or build upon the material, including for commercial use, providing the original author is credited.
References
Grajcar A., Różański M.: Spawalność wysokowytrzymałych stali wielofazowych AHSS, Przegląd Spawalnictwa nr 3/2014, s. 2227
Stano S.: Spawanie laserowe blach o zróżnicowanej grubości przeznaczonych na półfabrykaty karoserii samochodowych typu tailored blanks, Biuletyn Instytutu Spawalnictwa nr 2/2005, s. 2428
Górka J.: Weldability of thermomechanically treated steels having a high yield point, Archives of Metallurgy and Materials, Volume 60, Issue 1/2015, pp. 469475
Lisiecki A.: Diode laser welding of high yield steel. Proc. of SPIE Vol. 8703, Laser Technology 2012: Applications of Lasers, 87030S (January 22, 2013), DOI: 10.1117/12.2013429
Górka J.: Study of structural changes in S700MC steel thermomechanically treated under the influence of simulated welding thermal cycles, Indian Journal of Engineering and Materials Sciences, Vol. 22, October 2015, pp. 497502
Grajcar A., Różański M., Stano S.: Effect of heat input on microstructure and hardness distribution of laser welded Si-Al TRIP-type steel, Advances Material Science Engineering. 2014, Article ID 658947, pp. 18
Brózda J.: Nowoczesne stale konstrukcyjne i ich spawalność. Wydawnictwo Instytutu Spawalnictwa, Gliwice 2009
Górka J.: Własności i struktura złączy spawanych stali obrabianej termo- mechanicznie o wysokiej granicy plastyczności, Wydawnictwo Politechniki Śląskiej, Gliwice 2013
Y. Naito, S. Katayama, and A. Matsunawa.: Keyhole behaviour and liquid flow in molten pool during laser-arc hybrid welding, LAMP 2002 Proceedings, Volume 4831, pp. 357.
C. Bagger and F. Olsen.: Comparison of plasma, metal inactive gas (MIG) and tungsten inactive gas (TIG) processes for laser hybrid welding, Proceedings of ICALEO 2003, Jacksonville, FL, Oct. 1317, 2003, pp. 1120.
N.J. Orozco.: Fully integrated hybrid-laser welding control process, Processes for Laser Hybrid Welding, Proceedings of ICALEO 2003, Jacksonville, Fl, Oct. 1317, 2003, pp. 3140.
Murakami T., Shin M. H., Nakata K.: Effect of welding direction on weld bead formation in high power fiber laser and MAG arc hybrid welding, Transactions of JWRI 2/2010.