Structure of steel and cast steel resistance butt welded joints

##plugins.themes.bootstrap3.article.sidebar##

PDF
Opublikowane: lip 10, 2018
DOI: https://doi.org/10.26628/wtr.v90i7.939
Słowa kluczowe:
Hadfield cast steel, pearlitic steel, resistance butt welding, microstructure

##plugins.themes.bootstrap3.article.main##

Zbigniew Żurek
Akademia Górniczo-Hutnicza

Abstrakt

The paper presents the results of investigation of the microstructure of welded R260 steel with GX120Mn13 cast steel and X10CrNi18-8 steel. The analyzed materials had characteristic microstructure types. In the case of welded joints next to the fusion line, the phenomenon of liquid metal penetration along grain boundaries was observed, which is caused by the lower melting temperature of austenitic materials in relation to pearlitic steel. In addition, the heterogeneity of the chemical composition of austenitic materials related to the mixing of materials during welding was identified in this area.

Pobrania

Brak dostępnych danych do wyświetlenia.

##plugins.themes.bootstrap3.article.details##

Jak cytować
[1]
Z. Żurek, „Structure of steel and cast steel resistance butt welded joints”, Weld. Tech. Rev., t. 90, nr 7, lip. 2018.
Numer
Tom 90 Nr 7 (2018): WELDING TECHNOLOGY REVIEW
Dział
Original Articles

Creative Commons CC BY 4.0 https://creativecommons.org/licenses/by/4.0/

Artykuły czasopisma Welding Technology Review (Przegląd Spawalnictwa) publikowane są w otwartym dostępie na licencji CC BY (licencja Creative Commons Uznanie autorstwa 4.0 Międzynarodowe). Licencja CC BY jest najbardziej otwartą dostępną licencją i uważaną za „złoty standard” w formule otwartego dostępu; jest również preferowany przez wielu fundatorów badań. Licencja ta umożliwia czytelnikom kopiowanie i redystrybucję materiału na dowolnym nośniku i w dowolnym formacie, a także zmienianie, przekształcanie lub budowanie na nim materiału, w tym do użytku komercyjnego, pod warunkiem wskazania oryginalnego autora.

Bibliografia

Nikitin A. S.: Flash welding Hadfield steel to rail steel, Welding International, vol. 15 (3), 2001, pp. 217-219.

Zhang F., Lv B., Hu B., Li Y.: Flash butt welding of high manganese steel crossing and carbon steel rail, Materials Science and Engineering: A, vol. 454455, 2007, pp. 288-292.

Nikulina A. A., Bataev A. A., Smirnov A. I., Popelyukh A. I., Burov V. G., Veselov S. V.: Microstructure and fracture behaviour of flash butt welds between dissimilar steels, Science and Technology of Welding and Joining, vol. 20 (2), 2015, pp. 138-144.

Kuchuk-Yatsenko S.I., Didkovsky A.V., Shvets V.I., Antipin E.V., Wojtas P., Kozłowski A.: Flash-butt welding of high-strength rails, Mining Informatics, Automation and Electrical Engineering, vol. 528 (4), 2016, pp. 40-49.

Porcaro R. R., Paes de Lima D. A., Lúcio de Faria G., Godefroid L. B., Cândido L. C.: Microestrutura e Propriedades Mecânicas de um Aço para Trilhos Ferroviários Soldado por Centelhamento, Soldagem & Inspeção, vol. 22 (1), 2017, pp. 59-71.

Mansouri H., Monshi A.: Microstructure and residual stress variations in weld zone of flash-butt welded railroads, Science and Technology of Welding and Joining, vol. 9 (3), 2004, pp. 237-245.

PN-EN 13674-1+A1:2017-07 Kolejnictwo - Tor - Szyna - Część 1: Szyny kolejowe Vignolea o masie 46 kg/m i większej.

ISO 13521:2015 Austenitic Manganese Steel Castings.

PN-EN 10088-1:2014-12 Stale odporne na korozję - Część 1: Wykaz stali odpornych na korozję.