Abstrakt
The paper presents the results of non-destructive and destructive testing of the welded joint of the steam pipeline working under creep conditions. The purpose of this study is to describe the approach to assessment of technical condition of material of welded joints of hp steam pipelines in operation beyond the design work time and to de ne the methodology for assessing test results. The paper provides the results of destructive testing of the welded joint removed from the installation due to the negative results of non-destrutive testing. The analysis comprises metallographic examination by means of a scanning electron microscope, the evaluation of mechanical properties and abridged creep tests. Particular attention is paid to the in uence of quality of welded joints on operational safety of power equipment.
in polish
Diagnostyka złączy spawanych pracujących w warunkach pełzania
W referacie przedstawiono wyniki badań nieniszczących oraz niszczących złącza spawanego rurociągu parowego pracującego w warunkach pełzania. Opisano sposób podejścia do oceny stanu technicznego materiału złączy spawanych rurociągów wysokoprężnych pary pracujących powyżej obliczeniowego czasu pracy oraz metodykę oceny wyników badań. Przedstawiono wyniki badań niszczących złącza spawanego usuniętego z instalacji na podstawie negatywnych wyników badań nieniszczących. Analizy te obejmowały badania metalogra czne wykonane na mikroskopie skaningowym, badania własności mechanicznych oraz skrócone próby pełzania. Zwrócono uwagę na wpływ jakości wykonania złączy spawanych na bezpieczeństwo eksploatacji urządzeń energetycznych.
Pobrania
##plugins.themes.bootstrap3.article.details##
Creative Commons CC BY 4.0 https://creativecommons.org/licenses/by/4.0/
Artykuły czasopisma Welding Technology Review (Przegląd Spawalnictwa) publikowane są w otwartym dostępie na licencji CC BY (licencja Creative Commons Uznanie autorstwa 4.0 Międzynarodowe). Licencja CC BY jest najbardziej otwartą dostępną licencją i uważaną za „złoty standard” w formule otwartego dostępu; jest również preferowany przez wielu fundatorów badań. Licencja ta umożliwia czytelnikom kopiowanie i redystrybucję materiału na dowolnym nośniku i w dowolnym formacie, a także zmienianie, przekształcanie lub budowanie na nim materiału, w tym do użytku komercyjnego, pod warunkiem wskazania oryginalnego autora.
Bibliografia
Sprawozdania i wyniki prac pomiarowych i badawczych z lat 2014-2016, opracowania ENERGOPOMIAR Sp. z o.o., Zakład Chemii i Diagnostyki (niepubl.).
Dobrzański J.: Materiałoznawcza interpretacja trwałości stali dla energetyki, Open Access, Library, 2011, Vol. 3.
Hernas A., Dobrzański J.: Life-time and Damage of Boilers and Steam Turbines Elements, Publishing House of the Silesian University of Technology, Gliwice 2003.
Dobrzański J., Sroka M., Zieliński A.: Methodology of classi cation of internal damage the steels during creep service, Journal of Achievements in Materials and Manufacturing Engineering, 2006, vol. 18, pp. 263-266.
Zieliński A., Dobrzański J., Krztoń H.: Structural changes in low alloy cast steel Cr-Mo-V after long time creep service, Journal of Achievements in Materials and Manufacturing Engineering, 2007, vol. 25, Issue 1, pp. 33-36.
Dobrzański J., Krztoń H., Zieliński A.: Development of the precipitation processes in low-alloy Cr-Mo type steel for evolution of the material state after exceeding the assessed lifetime, Journal of Achievements in Materials and Manufacturing Engineering, 2007, vol. 23, Issue 2, pp. 19-22.
Zieliński A.: Wpływ długotrwałej eksploatacji w warunkach pełzania na własności mechaniczne staliwa Cr-Mo-V, VIII Międzynarodowa Konferencja Naukowa Nowe technologie i osiągnięcia w metalurgii i inżynierii materiałowej, Częstochowa 25 maja 2007, Wydawnictwo Politechniki Częstochowskiej, tom II, s. 717-721.
Zieliński, A., Dziuba-Kałuża, M., Dobrzański, J., Sroka M.: The impact of repair welded joint on the life of Cr-Mo-V steel steam pipeline after service under creep conditions, Materials Science and Engineering, 2014, vol. 68(1), pp. 36-44.
Dziuba-Kałuża, M., Dobrzański, J., Zieliński, A.: Mechanical properties of Cr-Mo and Cr-Mo-V low-alloy steel welded joints after long-term service under creep conditions, Archives of Materials Science and Engineering, 2013, vol. 63.1, pp. 5-12.
Sroka M., Zieliński A., Mikuła J.: The service life of the repair welded joint of Cr-Mo / Cr-Mo-V, Archives of Metallurgy and Materials, 2016, vol. 61, pp. 969-974.
Zieliński A., Golański G., Sroka M.: Comparing the methods in determining residual life on the basis of creep tests of low-alloy Cr-Mo-V cast steels operated beyond the design service life, International Journal of Pressure Vessels and Piping, 2017.
Instrukcja badań i oceny stanu technicznego rurociągów pracujących w warunkach pełzania, opracowanie ENERGOPOMIAR Sp. z o.o., Gliwice styczeń 2012 (niepubl.).
Jasiński A.: System diagnostyczny jako sposób na wydłużenie czasu bezpiecznej eksploatacji rurociągów parowych, Energetyka, 2012, nr 9.
Kwiecień M., Goławski A.: Pełzanie jako zjawisko ograniczające długotrwałą eksploatację rurociągów parowych, Energetyka, 2013, nr 7.
Jasiński A.: Jak typować elementy do badań w przypadku rurociągów wysokoprężnych, Energetyka, 2015, nr 9.
PN-75/H-84024: Rury stalowe bez szwu kotłowe, 1975.
PN-75/H-84024: Stal do pracy przy podwyższonych temperaturach
Gatunki, 1975.