Friction welding of ultrafine grained 316L steel
Article Sidebar
Main Article Content
Abstract
The article discusses the issues of weldability of metals with UFG (ultrafine grained) metals. The problem was discussed on the example of 316L steel with UFG structure obtained by metal forming method of hydrostatic extrusion. The joints were obtained by friction welding. Welding parameters were selected according to the criterion of the lowest degree of recrystallization of the joint area. Metallographic examinations were performed, selected areas of the joint welded in terms of hardness and range of softening of the material. Static tensile tests were carried out, the tensile strength of the parent material and the welded joint were compared.
in polish
Zgrzewanie tarciowe ultradrobnoziarnistej stali 316L
W artykule omówiono problematykę zgrzewalności metali o ultradrobnoziarnistej strukturze. Problem omówiono na przykładzie stali 316L o ultradrobnoziarnistej strukturze uzyskanej na drodze obróbki plastycznej hydrostatycznego wyciskania. Złącza uzyskano metodą zgrzewania tarciowego. Parametry zgrzewania dobierano wg kryterium najniższego stopnia rekrystalizacji obszaru złącza. Wykonano badania metalograficzne, scharakteryzowano wybrane obszary złącza zgrzewanego pod względem twardości i zasięgu zmiękczenia materiału. Wykonano próby statycznego rozciągania, porównano wytrzymałość na rozciąganie materiału rodzimego oraz złącza zgrzewanego.
Downloads
Article Details
Creative Commons CC BY 4.0 https://creativecommons.org/licenses/by/4.0/
Welding Technology Review (WTR) articles are published open access under a CC BY licence (Creative Commons Attribution 4.0 International licence). The CC BY licence is the most open licence available and considered the industry 'gold standard' for open access; it is also preferred by many funders. This licence allows readers to copy and redistribute the material in any medium or format, and to alter, transform, or build upon the material, including for commercial use, providing the original author is credited.
References
Hughes D.A. and Hansen N.: High angle boundaries formed by grain subdivision mechanisms, Acta Materialia, 9 (45), pp. 3871-3886, 1997.
Langdon T.G.: The impact of bulk nanostructured materials in modern research, Reviews on Advanced Materials Science, 25, pp. 11-15, 2010.
Kulczyk M., Przybysz S., Skiba J., Pachla W.: Severe Plastic Deformation Induced in Al, Al-Si, Ag and Cu by Hydrostatic Extrusion, Archives of Me- tallurgy and Materials, 59, pp. 59-64, 2014.
Pachla W., Skiba J., Kulczyk M., Przybysz S., Przybysz M., Wróblewska M., Diduszko R., Stępniak R., Bajorek J., Radomski M., Fąfara W.: Nanostructurization of 316L type austenitic stainless steels by hydrostatic extrusion, Materials Science and Engineering: A, vol. 615, oo, 116-127, 2014.
Garbacz H., Lewandowska M., Pachla W., Kurzydłowski K.: Structural and mechanical properties of nanocrystalline titanium and 316LVM steel processed by hydrostatic extrusion, Journal of Microscopy, vol. 223, pp. 272-274, 2006.
Salacinski T., Chmielewski T., Winiarski M., Cacko R., Świercz R.: Roughness of Metal Surface After Finishing Using Ceramic Brush Tools, Advances in Materials Science, vol. 18 (1), pp. 20-27, 2018.
Pietrzak K., Kaliński D., Chmielewski M., Chmielewski T., Włosiński W., Choręgiewicz K.: Processing of intermetallics with Al2O3 or steel joints obtained by friction welding technique, 12th Conference of the European Ceramic Society ECerS XII, Stockholm, 2011.
Ferenc K., Cegielski P., Chmielewski T.: Technika spawalnicza w praktyce, Poradnik inżyniera konstruktora i technologa, Verlag Dashofer, Warszawa, 2015.
Włosiński W., Chmielewski T., Kucharczyk M.: Spajanie tarciowe stopów NiAl i FeAl ze stalą węglową St3S, Przegląd Spawalnictwa vol. 76 (1), s. 6-12, 2004.
Hudycz M., Winiarski M., Chmielewski T.: Tarciowe metalizowanie ceramiki AlN tytanem, Przegląd Spawalnictwa, vol. 87 (10), s. 31-35, 2015.
Chmielewski T.: Wykorzystanie energii kinetycznej tarcia i fali detonacyjnej do metalizacji ceramiki, Prace Naukowe PW, seria Mechanika, Zeszyt 232, s. 1-155. 2012.