The influence of positioning deposited beads direction to resistance on grind wear plates abrasive wear
Article Sidebar
Main Article Content
Abstract
The article presents the results of the study of the significance of influence of positioning deposited beads towards direction of abrasive movement, to resistance on grind wear platesHARDPLATE 100S abrasive wear. The study on relevance of influence was conducted by using completely randomized design. The range of study has covered testing the metal-material abrasive wear resistance, macroscopic and microscopic metallographic examination and hardness tests.
Downloads
Article Details
Creative Commons CC BY 4.0 https://creativecommons.org/licenses/by/4.0/
Welding Technology Review (WTR) articles are published open access under a CC BY licence (Creative Commons Attribution 4.0 International licence). The CC BY licence is the most open licence available and considered the industry 'gold standard' for open access; it is also preferred by many funders. This licence allows readers to copy and redistribute the material in any medium or format, and to alter, transform, or build upon the material, including for commercial use, providing the original author is credited.
References
Bęczkowski R., Selected issues of applying a wear-resistant plates in the mining industry. Welding Technology Review, 2017, Vol. 89(5), 80-84. DOI: https://doi.org/10.26628/ps.v89i5.764
Mucha T., Bartkowiak K., Application of cladded abrasive-resistant plates in repairs of opencast mining equipment. Welding Technology Review, 2011, Vol. 83 (10), 73-76. DOI: https://doi.org/10.26628/ps.v83i10.473
Neale M., Gee M., A guide to wear problems and testing for industry, William Andrew, 2001, 3-8. DOI: https://doi.org/10.1016/B978-081551471-8.50002-5
Ban M., Hasegawa N., Ueno Y., Shinozaki H., Aoki T., Fukumoto H., Wear Resistance Property of Hardfacing Weld Overlays Containing Metal Carbides. Tribology Online 2012, Vol. 7(4), 207-212. DOI: https://doi.org/10.2474/trol.7.207
Czupryński A., Properties of Al2O3/TiO2 and ZrO2/CaO flame sprayed coatings. Spajanie Materiałów Konstrukcyjnych, 2017, Vol. 36(2), 32-39. DOI: https://doi.org/10.17222/mit.2015.165
Czupryński A., Kik T., Melcer M., Comparison of abrasion resistance of wear plates. Welding Technology Review, 2018, Vol. 90(5), 28-36. DOI: https://doi.org/10.26628/ps.v90i5.893
Klimpel A., Górka J., Czupryński A., Comparison of chromium cast iron deposits of wear plates. Journal of Achievements in Materials and Manufacturing Engineering, 2006, Vol. 18(1-2), 387-390.
Pawar S., Mukhopadhyay G., Metallurgical and Tribological Evaluation of Fe-Cr-C Hardfacing Alloys. Journal of
Failure Analysis and Prevention, 2018, Vol. 18(4), 868-876. DOI: https://doi.org/10.1007/s11668-018-0475-8
Turyk E., Riabcew I.A., Melcer M., Rebuilding of coils of screw conveyors with chromium cast iron hard laye.,
Welding Technology Review, 2018, Vol. 90(9), 24-27.
Varga M., High temperature abrasive wear of metallic materials. Wear, 2017, Vol. 376-377, 443-451. DOI: https://doi.org/10.1016/j.wear.2016.12.042
Yury K., Filiрpov M., Makarov A., Malygina I., Soboleva N., Fantozzi D., Adrea M., Koivuluoto H., Vuoristo P., Arc-Sprayed Fe-Based Coatings from Cored Wires for Wear and Corrosion Protection in Power Engineering. Coatings, 2018, Vol. 8(2), 71. DOI: https://doi.org/10.3390/coatings8020071
Ziemliński J., Simplified technology of welding large working surfaces exposed to the destructive effect of loose materials. (in-polish) Biuletyn Instytutu Spawalnictwa, 1966, Vol. 28, 28-32.
Welding Alloys Polska Sp. z o.o., Pad welded wear plates, WA, 2018.
Kukiełka L., Basics of engineering research. PWN, 2002, 40-42, 248.
https://www.random.org/sequences/?min=1&max=30&col=1&format=html&rnd=new (30.01.2019)