Effect of heat treatment on the properties and structure of steel 4330V
Article Sidebar
Main Article Content
Abstract
The article describes the effect of heat treatment of steel in the temperature range of 100÷900 °C on the structure and properties of tempered 4330V steel. The aim of the study was to investigate the behavior of steel under long heating without a protective atmosphere in the resistance furnace. This is an important aspect when you use this type of steel, when they are delivered to the customer in the running order after hardening and tempering. This allows you to determine what temperature it is possible to heat the steel 4330V in processes such as welding. After the process of heating test samples were tested for structural change, hardness and toughness. Carried out studies have shown a reduction in properties when temperature exceeds 600 °C during heat treatment. A significant drop in hardness to 275 HV was achieved. As a result of heating at a temperature of more than 800 °C there has been a hardening of the material in the air.
in polish
Wpływ obróbki cieplnej na własności i strukturę stali 4330V
W artykule opisano wpływ obróbki cieplnej polegającej na wygrzewaniu stali w zakresie temperatur 100÷900 °C na strukturę i własności stali ulepszonej cieplnie 4330V. Celem pracy było zbadanie zachowania się stali przy długim wygrzewaniu bez atmosfery ochronnej w piecu oporowym. Jest to ważny aspekt podczas wykorzystania tego typu stali, gdy są one dostarczane do odbiorcy w stanie gotowym po hartowaniu i odpuszczaniu. Dzięki temu można stwierdzić, do jakich temperatur możliwe jest podgrzanie stali 4330V w procesach łączenia takich jak spawanie. Po przeprowadzonym procesie wygrzewania badanie próbki zostały przebadane pod kątem zmian strukturalnych, twardości i udarności. Przeprowadzane badania wykazały zmniejszenie własności po przekroczeniu temperatury 600 °C podczas wygrzewania. Uzyskano znaczny spadek twardości do poziomu 275 HV. W wyniku wygrzewania w temperaturze ponad 800 °C nastąpiło zahartowanie materiału w powietrzu.
Downloads
Article Details
Creative Commons CC BY 4.0 https://creativecommons.org/licenses/by/4.0/
Welding Technology Review (WTR) articles are published open access under a CC BY licence (Creative Commons Attribution 4.0 International licence). The CC BY licence is the most open licence available and considered the industry 'gold standard' for open access; it is also preferred by many funders. This licence allows readers to copy and redistribute the material in any medium or format, and to alter, transform, or build upon the material, including for commercial use, providing the original author is credited.
References
S. Rudnik: Metaloznawstwo, Państwowe Wydawnictwo Naukowe, Warszawa 1980 r.
K. Przybyłowicz: Metaloznawstwo, Wyd. WNT, Warszawa 2007 r.
J. Adamczyk: Inżynieria wyrobów stalowych, Wyd. Politechniki Śląskiej, Gliwice 2000 r.
J. Pacyna, R. Dąbrowski: Wpływ wanadu na przemiany przy odpuszczaniu stali o małej zawartości innych pierwiastków,
conference proceedings AMME 2003, s. 713-717.
S. Sackl, M. Zuber, H. Cclemens, S. Primig: Induction tempering vs conventional tempering of a heat-treatable steel, Metallurgical and materials transactions a, vol. 47a.
A. Grajcar, M. Morawiec: Przegląd możliwości zastosowania nowoczesnych stali wysokowytrzymałych do produkcji walcówki na druty, Hutnik 2017 R. 84 nr 1, s. 6-10.
M. Gojić, L. Kosec, P. Matković: The effect of tempering temperature on mechanical properties and microstructure of low alloy Cr and CrMo steel, Journal of materials science 33, pp. 395-403.
J. Pilarczyk: Metaloznawstwo spawalnicze, Wyd. Politechniki Warszawskiej, Warszawa 1977r.
J. Pacyna, R. Dąbrowski: Wpływ wanadu na przemiany przy odpuszczaniu stali o małej zawartości innych pierwiastków, 12 th International Scientific Conference. Achivements in mechaanical and material engenering, pp. 713-718.
J. Górka: Własności i struktura złączy spawanych stali obrabianej termoplastycznie o wysokiej granicy plastyczności, Wyd. Pol. Śl., Gliwice 2013. [11] M. Żuk, J. Górka, A. Czupryński, M. Adamiak: Properties and structure of the weld joints of quench and tempered 4330v steel, Metalurgija vol. 55 iss. 4, pp.613-616.
AISI 4330V, TATA Steel, 2015r.
Certyfikat jakości stali 4330V.
www.westyorkssteel.com, Karta charakterystyki stali 4330V.