Cô° o-bô°ased bô°razing fillers
Article Sidebar
Main Article Content
Abstract
Cobalt-based superalloys are used under high-temperature service conditions. It is often necessary to join parts made of these alloys to construct components with complex geometries. High-temperature brazing is a suitable joining technology. To ensure a good corrosion resistance, the brazing filler and the base material should have similar chemical compositions. This paper deals with the development of near eutectic cobalt-based brazing fillers based on the alloy system Co-ZrC-TaC. The alloys are prepared by arc-melting on a water-cooled copper hearth in an argon atmosphere using a non-consumable tungsten electrode. Geometrical shaping is done by suction casting into a sectioned copper mould. Microstructure and melting behaviour are characterized by means of light microscopy and differential scanning calorimetry.
Luty na bazie kobaltu
Abstrakt
Nadstopy na bazie kobaltu są stosowane do pracy w wysokiej temperaturze. Często pojawia się konieczność łączenia elementów wykonanych z tych materiałów w celu uzyskania zaprojektowanej konstrukcji. Lutowanie twarde jest odpowiednią metodą łączenia tych stopów, ponieważ zapewnia dobrą odporność na korozję, przy czym zarówno materiał dodatkowy, jak i materiał lutowany powinny mieć taki sam skład chemiczny. W artykule przedstawiono wy- niki prac nad trójskładnikowym lutem przyeutektycznym opracowanym na bazie stopu kobaltu Co-ZrC-TaC. Stopy wytwarzane są przez topienie łukowe elektrodą wolframową na podkładce miedzianej chłodzonej wodą i w osłonie argonu. Kształt geometryczny nadawany jest w procesie odlewania próżniowego do dzielonej miedzianej formy. Mikrostruktura i zachowanie się topionego metalu analizowano z wykorzystaniem mikroskopii świetlnej i kalorymetrii skaningowej.
Downloads
Article Details
Creative Commons CC BY 4.0 https://creativecommons.org/licenses/by/4.0/
Welding Technology Review (WTR) articles are published open access under a CC BY licence (Creative Commons Attribution 4.0 International licence). The CC BY licence is the most open licence available and considered the industry 'gold standard' for open access; it is also preferred by many funders. This licence allows readers to copy and redistribute the material in any medium or format, and to alter, transform, or build upon the material, including for commercial use, providing the original author is credited.
References
Davies J. R.: nickel, cobalt and their alloys. ASM International, 2000.
Greaves W.: Kostengünstige Reparatur von Turbinenschaufeln durch Vakuum-Hartlöten. STR Sulzer Technical Review, 87 (2005) Issue 1, pp.19-21.
Falkenberg S.; Watermeyer K.: Die Untersuchung des Lötver- haltens von auf Ti-Al-Phasen aufgebauten Hochtemperatur- werkstoffen. Sonderbände der Praktischen Metallographie, 27 (1995), pp. 401-404.
Harvey D.: It Ìs a real gas for filler metals. Zusatzwerkstoffe für die Fertigung und Reparatur von Gasturbinenkomponenten. Welding and Metal Fabrication, 65 (1997) Issue 10, pp.14-18.
Heikinheimo L.; Miglietti W.; Kipnis J.; Leone E.; Rabinkin A.: Brazing of Co- and ni-based superalloys using new amorphous brazing filler metals, DVS-Berichte, 212 (2001), pp.30-34.
Acknowledgement
Donachie M. J.; Donachie S. J.: Superalloys: a technical guide, ASM International.
Greaves W.: Cost effective repairs for IGT vanes. Proceedings of the 3rd IBSC 2006, pp 392-394.
Shurin A. K.; Dmitrieva G. P.; Cherepova T. S.: Phase equilibria in Co-Me′C-Me′′C alloys. 1. systems with three-phase eutectic equilibrium, Powder Metallurgy and Metal Ceramics, 35 (1996), Issue 12, pp.615620.
Shurin A. K.; Dmitrieva G. P.; Cherepova T. S.: Phase Equili- bria in Co-MeC-MeC alloys. II. Systems with four-phase eutectic equilibrium, Powder Metallurgy and Metal Ceramics, 36 (1997), Issues 3-4, pp.193196.
Beckhoff B.: Handbook of Practical X-Ray Fluorescence Analysis, Springer Verlag, Berlin (2006).