Phase analysis of phase boundary zone for Hastelloy X with Palnicro 36M brazed joint
Article Sidebar
Main Article Content
Abstract
The article describes boundary zone for the Hastelloy X Palnicro 36M brazed joint, in which liquid brazing filler metal interacted directly with solid base metal. The main objective of the research was to analyze the microstructure of the border zone and to recognize the occurring phases. Methods used in the research were light microscopy, scanning electron microscopy (SEM) with EDS analysis and X-ray diffraction (XRD). In the phase boundary zone the following phases were identified: molybdenum nickel (Mo1.08Ni2.92), tetrataenite NiFe, chromium nickel (CrNi), boron chromium Cr5B3. Studies have also indicated the possibility of occurrence of phases based on Cr3NiB6 and Mo6(Ni0.75Si0.25)7 intermetallic compound in the phase boundary zone.
Downloads
Article Details
Creative Commons CC BY 4.0 https://creativecommons.org/licenses/by/4.0/
Welding Technology Review (WTR) articles are published open access under a CC BY licence (Creative Commons Attribution 4.0 International licence). The CC BY licence is the most open licence available and considered the industry 'gold standard' for open access; it is also preferred by many funders. This licence allows readers to copy and redistribute the material in any medium or format, and to alter, transform, or build upon the material, including for commercial use, providing the original author is credited.
References
Babul T., Jakubowski J., Kopeć J., et al: Lutowanie próżniowe uszczelnień ulowych w aparatach kierujących wykonanych ze stopów Hastelloy i Inconel z zastosowaniem lutu NiCrSiB, Przegląd Spawalnictwa, R. 79, nr 9, 2007, s.124-129.
Dul I.: Zastosowanie i przetwarzanie stopów niklu w przemyśle lotniczym, Przegląd Spawalnictwa R. 81, nr 7-8, 2009, s. 67-73.
Dul I., Kopeć J., Poradka A., et al: Wpływ wybranych czynników technologicznych na proces lutowania próżniowego stopów Ni i stali wysokostopowej 18-8, Przegląd Spawalnictwa R. 81, nr 10, 2009, s. 77-80.
Dul I., Jakubowski J., Senkara J.: Spajanie zaawansowanych stopów Ni w przemyśle lotniczym, Rudy i Metale Nieżelazne, 2011, s. 397-405.
Baranowski M., Jakubowski J.: Lutowność wybranych nadstopów niklu, Przegląd Spawalnictwa R. 86, nr 7, 2014, s. 3-8.
Eng R.D., Ryan E.J., Doyle J.R.: Nickel-base brazing ller metals for aircraft gas turbine application, Weld J, Miami; United States, 1977, 56:10.
Schwartz M.M.: Brazing, 2nd Editio, ASM International, Materials Park Ohio, 2003.
Sulzer Metco Braze Materials Guide, 2011.
Palnicro Data Sheet, 2013, http://www.morganbrazealloys.com/media/
/wesgo_metals_palniro_36m.pdf. Accessed 19 Oct 2017.
Bober M., Jakubowski J., Senkara J.: Badania zdolności kapilarnych lutu BNi2 metodą zmiennej szczeliny lutowniczej, Przegląd Spawalnictwa, R. 88, nr 9, 2016, s. 87-90, doi: 10.26628/PS.V88I9.663.
Edelmann F.: Characterization of the behavior of Palnicro brazing alloy for stainless steel joints, McGill University, 2005.
Turner D.: Évolution microstructurale des joints brass sur linconel 718 avecles alliages BNi-2 et PALNICRO, École de technologie suprieure, 2005.
Rokvam M.: Caractrisation De Microstructures De Joints Brass Avec Les Alliages Bcu-1, Bag-13a, Bau-4, Bau-6, Bni-1a, Bni-2, Bni-3 Et Palnicro 36M Ayant Pour Mtal De Base Un Superalliage Base Nickel, École de technologie suprieure, 2011.
Dul I., Senkara J., Bober M., Jakubowski J.: Wpływ wysokotemperaturowego wygrzewania próżniowego na lutowność Inconelu 718 lutem Palnicro 36, Przegląd Spawalnictwa R. 85, nr 9, 2013, s. 15-19.
Hastelloy X Composition, 2017, http://www.espimetals.com/index.php/ technical-data/82-Hastelloy X Composition, Accessed 19 Oct 2017.
Lugscheider E., Knotek O., Reimann H.: Das Dreistoffsystem Nickel-Chrom-Bor, Monatshefte für Chemie 105 s. 80-90, 1974, doi: 10.1007/BF00911291
Xiao C.B., Han Y.F.: Effect of silicon on microstructure and stress rupture properties at 1100 °C of yttrium modi ed Ni-Al-Mo-B alloy IC6, Journal of Mate- rials Science vol. 36, 2001, pp.1027-1030, doi: 10.1023/A:1004848528582