Using of Barkhausen noise in hardness evaluation of carburized and inductively tempered layers on AMS 6414 steel
Article Sidebar
Main Article Content
Abstract
The possibility of hardness changes determination of carburized and induction hardened layers using quantities describing Barkhausen noise quantitatively was analyzed. The studies were carried out on three samples of constant thickness of carburized layer (1.2 mm) with different hardness values. Measurements were made for three congurations of MEB4-C device provided by Mag-Lab s.c. that differed in magnetization frequency. The Barkhausen noise envelope and its characteristic parameters, energy, RMS, FFT periodograms and event distributions were analyzed. Interesting diagnostic correlations have been obtained which can be used to solve the non-destructive testing inverse problems.
in polish
Wykorzystanie szumu Barkhausena w ocenie twardości warstw nawęglanych oraz hartowanych indukcyjnie na stali AMS 6414
Analizowano możliwości określenia zmian twardości warstw nawęglanych i hartowanych indukcyjnie na podstawie wielkości ilościowo opisujących szum Barkhausena. Badania przeprowadzono na zestawie trzech próbek o stałej grubości warstwy nawęglanej (1,2 mm) o różnych wartościach twardości. Pomiary przeprowadzono dla trzech kon guracji aparatury MEB-4C Mag-Lab s.c. różniących się częstotliwością prądu magnesującego. Analizowano obwiednię szumu Barkhausena i jej punkty charakterystyczne, energię, RMS, periodogramy FFT oraz rozkłady liczby zdarzeń. Uzyskano interesujące korelacje diagnostyczne mogące posłużyć w rozwiązywaniu zagadnień odwrotnych badań nieniszczących.
Downloads
Article Details
Creative Commons CC BY 4.0 https://creativecommons.org/licenses/by/4.0/
Welding Technology Review (WTR) articles are published open access under a CC BY licence (Creative Commons Attribution 4.0 International licence). The CC BY licence is the most open licence available and considered the industry 'gold standard' for open access; it is also preferred by many funders. This licence allows readers to copy and redistribute the material in any medium or format, and to alter, transform, or build upon the material, including for commercial use, providing the original author is credited.
References
Moorthy V., Shaw B.A., Evans J.T. : Evaluation of tempering induced changes in the hardness pro le of case-carburised EN36 steel using magnetic Barkhausen noise analysis, NDT&E International, 36(1), pp. 43-49, 2003.
Stupakov O., Perevertov O., Tomas I., Skrbek B.: Evaluation of surface decarburization depth by magnetic Barkhausen noise technique, Journal of Magnetism and Magnetic Materials, 323(12), pp. 1692-1697, 2011.
Vourna P. , Ktena A., Tsakiridis P. E., Hristoforou E.: A novel approach of accurately evaluating residual stress and microstructure of welded electrical steels, NDT&E Int., Vol. 71, pp. 33-42, 2015.
Roskosz M., Fryczowski K.: Wykorzystanie szumu Barkhausena jako metody pomiaru twardości materiału ferromagnetycznego, Przegląd Spawalnictwa, Vol. 88, No 10, 2016, s. 143-145.
Kukla D., Piotrowski L., Szwed M.: Ocena twardości warstw nawęglanych i hartowanych indukcyjnie na stali AMS 6414 z zastosowaniem magnetycznych technik nieniszczących, Przegląd Spawalnictwa, Vol. 88, No 10, 2016, s. 46-50.