Pękanie spoin w procesie krzepnięcia
Article Sidebar
Main Article Content
Abstract
Scharakteryzowano mechanizmy powstawania pęknięć krystalizacyjnych w spoinach oraz w strefie wpływu ciepła, różnych stopów i podano możliwe sposoby ich ograniczenia.
Fracture of joints during solidification process
Mechanisms of crystallizing fracture formation in the joints and in the heat-affected zones in the case of various of alloys were charac- terised, and feasible methods were given to keep them within limits.
Downloads
Article Details
Creative Commons CC BY 4.0 https://creativecommons.org/licenses/by/4.0/
Welding Technology Review (WTR) articles are published open access under a CC BY licence (Creative Commons Attribution 4.0 International licence). The CC BY licence is the most open licence available and considered the industry 'gold standard' for open access; it is also preferred by many funders. This licence allows readers to copy and redistribute the material in any medium or format, and to alter, transform, or build upon the material, including for commercial use, providing the original author is credited.
References
Schabereiter H i inni: Możliwości unikania wad spowodowanych czynnikami metalurgicznymi przy spawaniu stali nierdzewnych, Materiały Seminarium Instytutu Spawalnictwa nt. Spawanie nowoczesnych gatunków stali, Czerwiec 1995.
Dupont J. N., Banovic S. W., Marder A. R.: Evolution and Weldability of Dissimilar Welds between a Super Austenitic Stainless Steel and Nickel-Based Alloys Weld. J. 82,2003.
Kou S.: Welding Metallurgy Wyd. Wiley Interscience, wyd. 2. 2003
Yang Y. P., Dong P., Zhang J., Tian X.: Weld. J. 79, 2000.
Pchennikov A., Streitenberger M., Herold H.: Kształtowanie i montaż dla jednostronnego spawania dużych elementów bez pęknięć krystalizacyjnych, Biuletyn Instytutu Spawalnictwa nr 6/2003.