Orbital TIG welding of X5CrNi18-10 austenitic stainless steel
Article Sidebar
Main Article Content
Abstract
The article presents the welding technology of pipe joints made of austenitic stainless steel X5CrNi18-10 with dimensions: ø 50,8 x 1,5 mm, made by TIG orbital welding method without the use of additional material. The following tests were carried out: chemical composition tests, delta ferrite content tests, non-destructive testing of welded joints, visual tests together with the assessment of tinge from the root side and weld face (according to the Danish Institute of Life Technology 94.34 report and the American ASME BPE standard 2012), radiographic examinations, destructive tests of welded joints. The tests have shown that the pro- posed technology allows to obtain welded joints that meet the requirements for the qualification of welding technology.
Downloads
Article Details
Creative Commons CC BY 4.0 https://creativecommons.org/licenses/by/4.0/
Welding Technology Review (WTR) articles are published open access under a CC BY licence (Creative Commons Attribution 4.0 International licence). The CC BY licence is the most open licence available and considered the industry 'gold standard' for open access; it is also preferred by many funders. This licence allows readers to copy and redistribute the material in any medium or format, and to alter, transform, or build upon the material, including for commercial use, providing the original author is credited.
References
Weman K.: A History of Welding, Svetsaren, 1, 2004, pp. 32-35.
Grundmann J.: Wysokowydajne spawanie cienkich blach TOPTIG(TM), Biuletyn Instytutu Spawalnictwa, Gliwice, 5, 2008, s. 69-71.
Kiszka A.: Spawanie orbitalne rur metodą TIG i A-TIG, Stal Metale & Nowe Technologie, 7-8, 2013, s. 63-66.
Aichele G.: Orbital welding solutions for demanding tasks (Part 1), Welding and Cutting, 4, 2005, pp. 176-178.
Nowacki J., Dąbrowski A., Łukojć A.: Technologiczne aspekty automatycznego spawania orbitalnego stali duplex, Przegląd Spawalnictwa, 8-10, 2002, s. 35-40.
Białucki P., Lange A., Miazga K.: Spawanie orbitalne rur cienkościennych ze stali 316L, Przegląd Spawalnictwa, 10, 2012, s. 33-35.
Niagaj J., Jędrusiak A.: Wpływ składu gazu osłonowego oraz parametrów spawania orbitalnego metodą TIG na wymiary i jakość spoin obwodowych rurek z austenitycznej stali nierdzewnej, Biuletyn Instytutu Spawalnictwa, 1, 2015, s. 25-29.
Lukkari J., Orbital TIG a great way to join pipes, vol. 60, Svetsaren, 1, 2005, pp. 3-6.
Parzych S., Pawłowski B., Krawczyk J., Bała.: Korozja wżerowa złączy spawanych stali austenitycznej X6CrNiTi18-10, Przegląd Spawalnictwa, 7, 2010, s. 14-17.
Łabanowski J., Głowacka M.: Przebarwienia powierzchni złączy spawanych stali odpornych na korozję, Przegląd Spawalnictwa, 6, 2008, s. 3-6.
Fydrych D.: Wpływ stanu powierzchni po spawaniu na odporność korozyjną austenitycznej stali nierdzewnej AISI 304, Biuletyn Instytutu Spawalnictwa 1,2018.
Menzel M.: Osłona grani spoiny, Przegląd Spawalnictwa, 6, 2008, s. 23-25.