Case studies of steel and their welded joint failures caused by liquid metal embrittlement LME

Main Article Content

Peter Bernasovsky
Peter Brziak
Lubos Mraz

Abstract

Liquid metal embrittlement (LME) is a phenomenon, where liquid (molten) metal is mostly intergranulary (but not only) penetrated into solid metal and causes its brit- tle fracture. The LME is usually related to low melting metals (zink, tin, cadmium) ,which are in the contact with higher molten ones (steels, Ni alloys). Cases of LME as a Cu penetration into pipeline welded joint of 15G2S steel ,a hot temperature corrosion in the cement works shell plate made of AISI 310 stainless steel attacted by Ni3S2 (Ts = 644 °C) and a vanadium corrosion in the boiler vessel (10CrMo9-10 steel) due to V2O5 + Na2SO4 eutecticum (~600 °C) are concerned. 

Analiza przypadków pęknięć stalowych złączy spawanych wywołanych obecnością cieczy metaliczne 

Streszczenie

Kruchość stali wywołana obecnością cieczy metalicznej (ang. LME liquid metal embrittlement) zachodzi podczas oddziaływania i w konsekwencji penetrowania granic ziaren (stali oraz stopów Ni) niskotopliwych metalami (cu, Zn, Col Sn), w warunkach działania naprężeń rozciągających. W artykule przeanalizowano przypadki LME wynikające z penetrowania Cu złączy spawanych rurociągów ze stali 15G29 oraz wysokotemperaturowej erozji płyt ze stali 310 wg ALSI wywołanej działaniem Ni3S2 (Ts-644 °C) oraz erozji kotła ze stali 10CrMo9-10 wywołanym oddziaływaniem w wysokiej temperaturze V2O5 + Na2SO4. 



Downloads

Download data is not yet available.

Article Details

How to Cite
[1]
P. Bernasovsky, P. Brziak, and L. Mraz, “Case studies of steel and their welded joint failures caused by liquid metal embrittlement LME”, Weld. Tech. Rev., vol. 87, no. 2, Feb. 2015.
Section
Original Articles

References

D.G. Kolman.: Environmentally Induced Cracking, Liquid Metal Embrittlement, ASM Handbook, Volume 13A, Corrosion: Fundamentals, testing and Protection, ASM International, Materials Park, OH pp. 381-392 (2003).

Liquid metal embrittlement, Metallurgical minutes, MAI, Summer 2004.

TWI Technical knowledge, Great Abington, UK, 2000.

D.G. Kolman.: Environmentally Induced Cracking, Solid Metal Embrittlement, ASM. Handbook, Volume 13A, Corrosion: Fundamentals, testing and Protection, ASM International, Materials Park, OH pp. 393 - 397 (2003).

Bernasovský,P. Brziak,P.: Case study of 15G2S grade gas pipeline. Technical. report, VÚZ-PI SR, ME 103, Bratislava, June 2003.

Bernasovský, P.- Brziak, P.: Analysis of AISI 310 steel plate. Technical report, VÚZ-PI. SR, ME 148, Bratislava, 31.5.2007.

Mráz, Ľ. et al.: Analysis of 33,7x5 mm pipe made of 10VrMo 9-10 steel in boiler K3. Technical report , VÚZ - PI SR, ME 068, Bratislava, 13.4.2012.

Andijani, J.-Malik, A.U.: Sulfur and vanadium induced hot corrosion of boiler tubes. Chemistry & Industry Conference, Riyadh, Dec. 11-15, 2004.